Your daily dose of Photovoltaic Technology Developments and Solar News

• Most Popular Articles

  • Top Stories 2008 – Power Generation – the good, the bad, and the efficiency
  • Top stories 2008 – Materials – could UMG be the answer?
  • Acciona’s Portuguese PV plant may be big, but one of the numbers just doesn’t add up
  • Top Stories 2008 - Thin Film – orders, gigawatts and growth
  • Top Stories 2008 – Cell Processing – efficiency is the name of the game!

• Editor's Picks

  • Top stories 2008 – Materials – could UMG be the answer?
  • Massive 168% photovoltaic module overcapacity to cause pricing collapse in 2009
  • Solar Santa: Ohio doles out millions in development dollars to local PV companies
  • Recession, what recession? Cavalcade of solar PV, renewable investments total billions in a day
  • Total taps into Konarka with US$45 million investment & R&D pact

• Latest Videos

  • Canadian Solar VP Robert Patterson talks Umg Si product lines - 150MW-plus in 2009
  • Delivering gasses for rapid growth in the PV Industry - Linde Electronics
  • Secrets of turnkey PV Module lines with Spire CEO Roger Little
  • Large area thin-film modules approach scale manufacturing with Applied Materials and Signet Solar
  • A passion for solar change: Anton Milner, Q-Cells CEO - exclusive interview

By G. TamizhMani, B. Li, T. Arends, J. Kuitche, B. Raghuraman, W. Shisler, K. Farnsworth, J. Gonzales, & A. Voropayev,
Arizona State University Photovoltaic Testing Laboratory (ASU-PTL), Mesa, Arizona, USA

ABSTRACT
Design and performance qualification testing of PV modules consists of a set of well-defined accelerated stress tests with strict pass/fail criteria. ASU-PTL is an ISO 17025-accredited testing laboratory and has been providing photovoltaic testing services since 1992. This paper presents a failure analysis on the design qualification testing of both crystalline silicon (c-Si) and thin-film technologies for two consecutive periods: 1997-2005 and 2005-2007. In the first period, the industry was growing at a slower rate with traditional manufacturers, with qualification testing of c-Si technologies being primarily conducted per Edition 1 of the IEC 61215 standard. In the second period, the industry was growing at an explosive rate with new manufacturers joining the traditional manufacturers, while qualification testing of c-Si was primarily conducted per Edition 2 of IEC 61215. Similar failure analysis according to IEC 61646 has also been carried out for thin-film technologies. The failure analysis of the test results presented in this paper indicates a large increase in the failure rates for both c-Si and thin-film technologies during the period of 2005-2007.