SunPower to construct largest power plant in the U.S. for Florida Power & Light Company - 10 July 2008
Applied Materials gains first Italian ‘SunFab’ customer - 09 July 2008
Canadian Solar commits to five new contracts totalling 14.9MW - 07 July 2008
Applied Materials breaks ground at Singapore Operations Center - 08 July 2008
Thin-film start-up Sencera invests $36.8 million in 38MW plant - 08 July 2008
REC ASA enters several silane supply deals worth close to $1 billion - 18 July 2008
Analysts eye tighter subsidies in Spain for solar industry - 18 July 2008
Global market leader SMA Solar Technology AG accelerates time-to-market with Across - 18 July 2008
Solar gains in popularity - 18 July 2008
Solar panels to join backup power plant at West Side facility - 18 July 2008
IMEC has claimed a breakthrough in crystalline Si
solar cell efficiencies that have reached an efficiency of 17.4 percent
with the potential to scale to efficiencies above 20 percent with a
decrease in cell thicknesses, according to the R&D centre based in
Leuven, Belgium.
The breakthrough comes from several years of research
into a new cell concept dubbed ‘i-PERC’ (Passivated Emitter and Rear
Cell). The PERC technology was not previously applicable to volume
production solar cell applications; however the ‘i’ addition denotes
‘industrial’ use.
According to IMEC, the new process uses very thin
silicon layers (<180µm) in which the classical Al back surface
field, covering the whole rear of the Si solar cell, is replaced by
local Al-alloyed contacts. In this process the rear is passivated by a
dielectric stack, in which the contact openings are realized by laser
ablation. Subsequently, an Al contact layer is evaporated which is
fired in a belt-line furnace to create local back-surface fields.
IMEC also developed small-area crystalline Si solar cells with evaporated contacts. Lab-scale silicon solar cells have been realized, where for the first time the i-PERC process has been used as a method to passivate the rear side and to create local contacts. At the front side random pyramids are used in combination with a standard silicon nitride layer to provide good optical properties and surface passivation.
The evaporated Ti/Pd/Ag front contact grid is patterned by standard lithography. First attempts immediately resulted in an efficiency of 19% with an impressive short-circuit current of more than 39mA/cm2, IMEC said.